Performance Beryllium bronze hardness is between (HRC) 38-43, density 8.3g / cm3, containing beryllium 1.9% -2.15%, it is widely used in plastic insert injection mold inner inserts, cores, die-casting punches, hot runners Cooling systems, thermal nozzles, integral cavities for blow molds, automotive molds, wear plates, etc.
Through in-depth research on the internal causes of failure, composition and resistance to liquid metal erosion of beryllium bronze mold materials, a combination of high electrical conductivity (thermal), high strength, abrasion resistance, high temperature resistance, high toughness, and resistance to metal liquid erosion has been developed. High-performance beryllium bronze mold material.
Solve the domestic non-ferrous metal low pressure, gravity casting mold easy cracking, wear and other problems, significantly improve the mold life, demolding speed and casting strength; overcome the metal slag adhesion and erosion of the mold; improve the casting surface quality; reduce Production cost; make the life of the mold close to the level of imports.
Through in-depth research on the internal causes of failure, composition and resistance to liquid metal erosion of beryllium bronze mold materials, a combination of high electrical conductivity (thermal), high strength, abrasion resistance, high temperature resistance, high toughness, and resistance to metal liquid erosion has been developed. High-performance beryllium bronze mold material.
Solve the domestic non-ferrous metal low pressure, gravity casting mold easy cracking, wear and other problems, significantly improve the mold life, demolding speed and casting strength; overcome the metal slag adhesion and erosion of the mold; improve the casting surface quality; reduce Production cost; make the life of the mold close to the level of imports.